Loading presentation...

Present Remotely

Send the link below via email or IM

Copy

Present to your audience

Start remote presentation

  • Invited audience members will follow you as you navigate and present
  • People invited to a presentation do not need a Prezi account
  • This link expires 10 minutes after you close the presentation
  • A maximum of 30 users can follow your presentation
  • Learn more about this feature in our knowledge base article

Do you really want to delete this prezi?

Neither you, nor the coeditors you shared it with will be able to recover it again.

DeleteCancel

Make your likes visible on Facebook?

Connect your Facebook account to Prezi and let your likes appear on your timeline.
You can change this under Settings & Account at any time.

No, thanks

All Ceramic

올세라믹 정리
by

son hyunlak

on 25 July 2013

Comments (0)

Please log in to add your comment.

Report abuse

Transcript of All Ceramic

도자기
토기
A.D 1000년경 중국
1717년 유럽에 전파
Metal free Restoration
사회 환경의 변화
심미성에 대한 높은 요구
환자의 경제력 변화
재료특성의 우선순위 변화
교합기능의 회복
심미성의 회복
Metal Allergy
도재의 성분
Matrix (유리질)
Filler (입자)
장석(feldspar) : 75~85%
석영(quartz) : 12~22%
고령토(Al O -2SiO - 2H O) : 4%
2
3
2
2
Microline + Albite
(K O-Al O -6SiO ) (Na O-Al O -6SiO )
2 2 3 2
2 2 3 2
도재 고유의 반투명성을 부여
1250~1500도까지 가열
서로 융합후 유리상 형성
강화재
기질을 유지 및 안정화
Binder(결합재)
성형성, 조작성
불투명, 소량존재
도재분말 제조법
fritting, frit
혼합, 가열, 급냉
분말
유리기질에 알루미나 결정(50%) 분산
불투명 - 내부 core용
40%이상 강도 증가
McLean, Huges
Vident
알루미나 85% + 유리질 15%
굴곡강도 : 500 MPa
최근 : CAD/CAM, Slip Cast 병용
투명도를 높여 심미성을 개선
알루미나 MgAl O
2 4
굴곡강도 : 350 MPa
Single Cr.
Ivoclar Vivadent
굴곡강도 : 119 MPa
심미성, 변연적합성 우수
Leucite(백류석) + 유리질
Core / 치관 전체
layering tech./ staining tech.
Empress 1 대구치 파절
Lithium disilicate ( Li - SiO - O ) + 유리질
2 2 5
굴곡강도 : 302 MPa
전치부 3unit, 구치부 single cr
Empress 1 개량
Single Cr 만 타겟
심미성 강조
ingot pressing 후 cut back, build up
Dentin
Porcelain
Collagen fiber
unfilled resin
silane
Resin
primer
Transformation Toughening
Zirconia
ZrO (산화지르코늄)
2
우수한 생체 친화성, 고강도(PFZ)
임시합착이 가능
변색을 차단하는 능력
도재처리
치면처리
1. Etching
2. Primer
3. Adhesive Resin
4. Resin Cement (Dual Cure)
1. 불산처리 (9% - 1분, 5% - 4분), 초음파 세척
2. 실란처리 후 열처리
All Ceramic
3. Resin Cement (Dual Cure)
Zirconia
In-Ceram
Empress
CAD/CAM
CEREC
Silane
Hot-Pressed
LAVA
e. max CAD
Ingot
도기
자기
thank you for your attention~
1. 100% 치밀한 sintered zirconia를 직접 milling 하는 방법
2. 부분적으로 소성된 50% 치밀한 zirconia를 milling하는 방법
크고 복잡한 machine이 필요
한개의 coping을 milling하는데 2~4시간 소요
sintering 과정이 필요없기 때문에 shrinkage가 없다.
milling 시간이 길고 bur의 손실이 크다.
ex) Digident
milling 후 단단하게 하기 위해 6~8시간 동안 firing 해야 함
firing 과정에서 shrinkage 발생 (20%)
software로 적절한 수축의 정도를 보상하는 것이 성공의 관건
ex) Vita YZ, Ceron, Lava
CAD/CAM
1. CAD
2. CAM
디자인까지 담당하는 software
CAD에서 넘겨받은 디자인을 밀링 가공할수 있는 데이터로 변환하는 software